Non Ferrous Powders

Non Ferrous Premix

Product group dedicated to sintering of bronze parts

Process: atomisation of pure metals, sieving, homogenisation
Composition: Sn 8 to 11%; Zn can be added, lubricant, graphite and other.
Apparent densities: 1.80 g / cm3 up to 3.40 g / cm3
Particle shape: irregular to partially spongy
Particle size distribution: 350 to 25 microns
Colour: greenish yellow

Product families

Bronze PMX 500
Powder blend of Cu and Sn with additions of elements i.e. Zn, Graphite, lubricant according to customised specification
Description of the material and main chemical components

Powder blend of Cu and Sn with additions of elements i.e. Zn, Graphite, lubricant according to customised specification

Description of the manufacturing process

Blending and homogeneisation, custom testing

Typical applications

Non ferrous sintering

Particle shape

Various

Main characteristic

Use of blends made of pure metals is normally preferred solution because of the flexibility in definition of final product characteristics

Particle upper cut size (full range)

106 to 180

Particle upper cut size (typical)

150

Apparent density (typical)

150

Application notes

Products are ready to press

Type Upper cut size(µm) Apparent density(g/cm3) Added elements Green strength (N/mm2)
PMX 550 106 2.9 Sn at 10%, C at 0,4%, lub 0,4% 5,0 min
PMX 551 106 3 Sn at 10%, lub at 0,5% 4,0 min
PMX 552 106 2.9 Sn at 10%, C at 0,2%, lub 0,6% 4,0 min
Diamond tools Premixes
Premix blend ready to press for free sinter/hot pressing
Description of the material and main chemical components

Premix blend ready to press for free sinter/hot pressing

Description of the manufacturing process

Blend of qualified powders

Typical applications

Diamond tools and hard metals

Particle shape

Various

Main characteristic

Ready to press composition

Particle upper cut size (full range)

tbd

Particle upper cut size (typical)

tbd

Application notes

Products are ready to press

Type Upper cut size(µm) Added elements
DT 201 tbd
DT 301 tbd
FeP15 4 P at 15%
Infiltration Cu IN
Powder blend of Cu (main) with Fe and other metals
Description of the material and main chemical components

Powder blend of Cu (main) with Fe and other metals

Description of the manufacturing process

Blending and homogeneisation

Typical applications

Ferrous sintering (for the particular process defined "Infiltration")

Particle shape

Variuous

Main characteristic

Composition specific to "infiltratrion" process

Particle upper cut size (full range)

180

Particle upper cut size (typical)

180

Apparent density (typical)

3

Application notes

Products are ready to press

Type Upper cut size(µm) Apparent density(g/cm3) Added elements Flowability (s/50g)
CUIN 200 106 3 Mn at 0,6%, Fe at 2% 45 max
CU IN L301 212 3.25 Mn at 1%, Fe at 2,3%