Process: water atomisation of molten alloy, sieving
Composition: Zn at 30%
Apparent densities: 2.55 g / cm3 up to 3.20 g / cm3
Particle shape: irregular
Particle size distribution: 500 to 45 microns
Colour: greenish yellow
| Description of the material and main chemical components | Brass Powder made with 20% Zn |
|---|---|
| Description of the manufacturing process | Water atomisation from molten alloy, sieving |
| Typical applications | Non ferrous sintering, friction, filler |
| Particle shape | Irregular to rounded |
| Particle upper cut size (full range) | 150 |
| Particle upper cut size (typical) | 150 |
| Apparent density (typical) | 3.25 |
| Application notes | Brass is used in sintering for parts with modest mechanical characteristics requiring oxidation resistance. In friction applications it is appreciated for thermal conductive characteristic and lubricant effect. Specific gold colour is often a reason of choice either in sintering and in filler use |
| Type | Upper cut size(µm) | Apparent density(g/cm3) |
|---|---|---|
| OT 150 | 150 | 3.25 |
| Description of the material and main chemical components | Brass Powder made with 30% Zn |
|---|---|
| Description of the manufacturing process | Water atomisation from molten alloy, sieving |
| Typical applications | Non ferrous sintering, friction, filler |
| Particle shape | Irregular to rounded |
| Main characteristic | Lower hardness, good machinability, lower mechanical preformances, higher resistance to oxidation over time (compared to sintered bronze) |
| Particle upper cut size (full range) | 63 to 1000 |
| Particle upper cut size (typical) | 63 to 1000 |
| Apparent density (typical) | 2,55 to 3,20 |
| Application notes | Brass is used in sintering for parts with modest mechanical characteristics requiring oxidation resistance. In friction applications it is appreciated for thermal conductive characteristic and lubricant effect. Specific gold colour is often a reason of choice either in sintering and in filler use |
| Type | Upper cut size(µm) | Apparent density(g/cm3) |
|---|---|---|
| OT 1000 | 1000 | 2.55 |
| OT 212 | 250 | 3.2 |
| OT 212/63 | 212 | 2.65 |
| OT 63 | 63 | 3.2 |