Focussed on the specific need of providing sintering manufacturers, ready to press blends, Pometon has developed products and process to mix the several elements of customised recipes and to guarantee appropriate quality of the supply.
Over 100 different blends are today defined to meet customers requirements for material press ready powder. Each blend requires a very close cooperation between Customer and Pometon technicians in the definition of parameters and control methods.
Description of the material and main chemical components | Blend of iron powder (type Fersint RI) with lubricants and graphite in custom tailored % |
---|---|
Description of the manufacturing process | Blending, homogeneisation |
Typical applications | Sintering of ferrous parts |
Particle shape | Various |
Main characteristic | Product is result of codesign process of the blend. Pometon grants constancy of processing parameters and testing method |
Particle upper cut size (full range) | 180 to 212 |
Particle upper cut size (typical) | 180 to 212 |
Apparent density (typical) | 3,0 to 3,2 |
Application notes | Each variance is unique to its customer on % and type of the composants but also in the definition of final testing method |
Recommended packaging | BB 1000 |
Type | Upper cut size(µm) | Base material | Added metal powders | Green strength (N/mm2) |
---|---|---|---|---|
107 | 180 | RI 180/3,0 | Cu at 1%, C at 0,5% | 9,0 min |
130 | 180 | RI 180/3,0 | Cu at 2,2%, C at 0,6% | 10 min |
301 | 180 | RI 180/3,0 | Cu at 3%, MnS at 0,5%,C at 0,7% | 9,0 min |
Description of the material and main chemical components | Blend of iron alloy (type DB1-2, ST0-1-2-3 or Ni2) with lubricants and graphite in custom tailored % |
---|---|
Description of the manufacturing process | Blending, homogeneisation |
Typical applications | Sintering of ferrous parts |
Particle shape | Various |
Main characteristic | Product is result of codesign process of the blend. Pometon grants constancy of processing parameters and testing method |
Particle upper cut size (full range) | 180 to 212 |
Particle upper cut size (typical) | 180 to 212 |
Apparent density (typical) | 3,0 to 3,2 |
Application notes | Each variance is unique to its customer on % and type of the composants but also in the definition of final testing method |
Recommended packaging | BB 1000 |
Type | Upper cut size(µm) | Base material | Added metal powders | Green strength (N/mm2) |
---|---|---|---|---|
202 | 180 | DB1 | C at 0,6% | 10 min |
209 | 180 | Ni2 | Cu at 1%, C at 0,3% | 10 min |
210 | 180 | DB2 | C at 0,2% | 14 min |