Iron-Phospour powders are Especially designed for sintering applications.
Theese pre-alloyed powders guarantee higher mechanical strenght with lower sintering temperatures.
| Description of the material and main chemical components | Blend of iron powder (type Fersint RI) with Iron-Phosphour alloy powder |
|---|---|
| Description of the manufacturing process | Mix and homogenisation of two iron powders |
| Typical applications | Sintering of Ferrous components without major mechanical performances |
| Particle shape | Irregular |
| Main characteristic | Presence of FeP permit a to form a blend suitable to pressing with no addition of other metals. Final performance being much higher compared to Basic iron powders if pressed without alloying metals |
| Particle upper cut size (full range) | 180 |
| Particle upper cut size (typical) | 180 |
| Apparent density (typical) | 3.15 |
| Application notes | Thermal treatments are rarely applied to this material. It is normally used with addition of lubricant an modest/none graphite |
| Recommended packaging | BB 1000 |
| Type | Upper cut size(µm) | Ot % | Apparent density(g/cm3) | Added elements |
|---|---|---|---|---|
| P 45 | 180 | 0.15 | 3,05 to 3,25 | P at 0,45% |
| P60 | 180 | 0.15 | 3,05 to 3,25 | P at 0,60% |