A range of innovative, environmentally friendly, copper-free metal powders. These products share a common basic concept but different thermomechanical properties. This translates into distinct behaviours during braking action, achieving the best performance and comfort.
Description of the material and main chemical components | Alloy of iron Sn atomised powder |
---|---|
Description of the manufacturing process | Water atomisation of molten alloy, annealing, mechanical treatment and final sieving |
Typical applications | NAO and sintered brakepads |
Particle shape | Various |
Main characteristic | Product specifically designed for friction applications and Cu free |
Particle upper cut size (full range) | 212 |
Particle upper cut size (typical) | 212 |
Apparent density (typical) | 2.5 |
Application notes | Can be used both in sintered or organic brakes |
Recommended packaging | L20 P400 |
Type | Upper cut size(µm) | Ot % | Added elements |
---|---|---|---|
Brakealloy S | 250 | 0.4 | Sn at 30% |
Description of the material and main chemical components | Alloy of iron Sn/Bi atomised powder |
---|---|
Description of the manufacturing process | Water atomisation of molten alloy, annealing, mechanical treatment and final sieving |
Typical applications | NAO and sintered brakepads |
Particle shape | Various |
Main characteristic | Product specifically designed for friction applications and Cu free |
Particle upper cut size (full range) | 212 |
Particle upper cut size (typical) | 212 |
Apparent density (typical) | 2.7 |
Application notes | Can be used both in sintered or organic brakes |
Recommended packaging | L20 P400 |
Type | Upper cut size(µm) | Ot % | Added elements |
---|---|---|---|
Brakealloy SB | 250 | 0.4 | Sn at 17%, Bi at 13% |
Description of the material and main chemical components | Alloy of iron Zn atomised powder |
---|---|
Description of the manufacturing process | Water atomisation of molten alloy, annealing, mechanical treatment and final sieving |
Typical applications | NAO and sintered brakepads |
Particle shape | Various |
Main characteristic | Product specifically designed for friction applications and Cu free |
Particle upper cut size (full range) | 212 |
Particle upper cut size (typical) | 212 |
Apparent density (typical) | 2.1 |
Application notes | Can be used both in sintered or organic brakes |
Recommended packaging | L20 P400 |
Type | Upper cut size(µm) | Ot % | Added elements |
---|---|---|---|
Brakealloy Z | 250 | 0.4 | Zn at 21,5% |