Materials » Non Ferrous Powders » Copper Powders » Copper Atomised powder

Copper Atomised powder
  • Copper Atomised powder
  • Production technique: water atomization, sieving
  • Composition: 99,00% to 99.6%
  • Apparent densities: 2.00 g / cm3 up to 3.30 g / cm3
  • Particle shape: spherical to irregular
  • Particle size distribution: 425 to 45 microns
Copper W-PM-CUE
Copper W-PM-CUE

Product Group: Copper Atomised powder
Description of the material and main chemical components:Copper powder attained from melting of qualified copper raw material
Description of the manufacturing process:water atomisation from refined molten bath, sieving
Typical applications: Ferrous sintering, Non ferrous sintering, brazing, filler, friction, catalyst
Main characteristic of the product Type:Atomised copper is most convenient choice when no specific reasons impose the use of lowest grades or dendritic shape typical to electrolytic powders
Particle shape:from spherical to irregular
Particle upper cut size (Full range): 60 to 425
Particle upper cut size (Typical):60 to 425
Apparent density (Typical):2.20 to 3.30
Recommended Pakaging:
Application notes:In ferrous sintering it is used as additive to adjust characteristics, In non ferrous it is used as main component in its reduced form.
Key elements: Cu copper
Key Processing: Atomisation: powder

Other grades are available

Common Version:
grade sieving size Cu content % min Ot% apparent density
CU W 425/75 425 99.5 0.2 2.8
CU W RCP 150 99.6 0.2 2.7
CU PM100 100 99.0 0.2 2.4

 

Copper CuDr150
Copper W-PM-CUE

Product Group: Copper Atomised powder
Description of the material and main chemical components:Copper powder attained from melting of qualified copper raw material
Description of the manufacturing process:water atomisation from refined molten bath, sieving
Typical applications: Friction, filler
Main characteristic of the product Type:Specific particle size distribution
Particle shape:irregular
Particle upper cut size (Full range): 150
Particle upper cut size (Typical):150
Apparent density (Typical):2.8
Recommended Pakaging:
Application notes:
Key elements: Cu copper
Key Processing: Annealing, Atomisation: powder

Other grades are available

Common Version:
grade sieving size Particle size <45 Cu content% min apparent density
CuDr150 150 60 to 80% 99,5 2,8

 

Models Copper W-PM-CUE Copper CuDr150
Fe iron  
Cr chromium  
P phosphorous  
Ni nickel  
Mn manganese  
Cu copper
Cu (elctrolytic)  
Mo molybdenum  
Zn zinc  
Sn tin  
Various Premix additive  
AI aluminium  
tiO2 titanium dioxide  
Models Copper W-PM-CUE Copper CuDr150
Annealing 
Diffusion Bonding  
Atomisation: powder
Atomisation: granules  
Electrolytic Powder  
Crushing  
Mixed/Homogenised powder (ready to use)  
Model Copper W-PM-CUE Copper CuDr150
Sintering 
Friction
Blasting  
Diamonds Tool  
Welding  
Flame cutting  
Plastic/resin/ceramic filler
Carbon brush  
Chemical  
Jewellery  
Food/Pharmaceutical/Cosmetics  
Magnetic  
Brazing 
Other iron applications  
Soft Blasting