Materials » Non Ferrous Powders » Other Non Ferrous Powders » Non Ferrous Premix
- Non Ferrous Premix
- Product group dedicated to sintering of bronze parts
- Process: atomisation of pure metals, sieving, homogenisation
- Composition: Sn 8 to 11%; Zn can be added, lubricant, graphite and other.
- Apparent densities: 1.80 g / cm3 up to 3.40 g / cm3
- Particle shape: irregular to partially spongy
- Particle size distribution: 350 to 25 microns
- Colour: greenish yellow
Bronze PMX 500
Infiltration Cu IN
| Product Group: | Non Ferrous Premix |
| Description of the material and main chemical components: | Powder blend of Cu and Sn with additions of elements i.e. Zn, Graphite, lubricant according to customised specification |
| Description of the manufacturing process: | Blending and homogeneisation, custom testing |
| Typical applications: | non ferrous sintering |
| Main characteristic of the product Type: | Use of blends made of pure metals is normally preferred solution because of the flexibility in definition of final product characteristics. |
| Particle shape: | various |
| Particle upper cut size (Full range): | 106 to 180 |
| Particle upper cut size (Typical): | 150 |
| Apparent density (Typical): | 150 |
| Recommended Pakaging: | |
| Application notes: | Products are ready to press. |
| Key elements: | Cu copper, Cu (elctrolytic), Zn zinc, Sn tin, Various Premix additive |
| Key Processing: | Atomisation: powder, Electrolytic Powder, Mixed/Homogenised powder (ready to use) |
Other grades are available
| grade | sieving | added elements | apparent density | Green strenght (N/mm2) |
| PMX 550 | 106 | Sn at 10%, C at 0.4%, lub 0.4% | 2.9 | 5.0 min. |
| PMX 551 | 106 | Sn at 10%, lub at 0.5% | 3 | 4.0 min |
| PMX 552 | 106 | Sn at 10%, C at 0.2%, lub 0.6% | 2.9 | 4.0 min |
| Product Group: | Non Ferrous Premix |
| Description of the material and main chemical components: | Powder blend of Cu (main) with Fe and other metals |
| Description of the manufacturing process: | Blending and homogeneisation |
| Typical applications: | Ferrous sintering (for the particular process defined "Infiltration") |
| Main characteristic of the product Type: | Composition specific to "infiltratrion" process |
| Particle shape: | variuous |
| Particle upper cut size (Full range): | 180 |
| Particle upper cut size (Typical): | 180 |
| Apparent density (Typical): | 3 |
| Recommended Pakaging: | |
| Application notes: | Products are ready to press. |
| Key elements: | Cr chromium, Mn manganese, Cu (elctrolytic), Various Premix additive |
| Key Processing: | Atomisation: powder, Electrolytic Powder, Mixed/Homogenised powder (ready to use) |
Other grades are available
| grade | sieving size | added elements | apparent density | Flowability |
| CUIN 200 | 106 | Mn at 0.6%, Fe at 2% | 3 | 45 max |
| Models | Bronze PMX 500 | Infiltration Cu IN |
| Fe iron | ||
| Cr chromium | • | |
| P phosphorous | ||
| Ni nickel | ||
| Mn manganese | • | |
| Cu copper | • | |
| Cu (elctrolytic) | • | • |
| Mo molybdenum | ||
| Zn zinc | • | |
| Sn tin | • | |
| Various Premix additive | • | • |
| AI aluminium | ||
| tiO2 titanium dioxide |
| Models | Bronze PMX 500 | Infiltration Cu IN |
| Annealing | ||
| Diffusion Bonding | ||
| Atomisation: powder | • | • |
| Atomisation: granules | ||
| Electrolytic Powder | • | • |
| Crushing | ||
| Mixed/Homogenised powder (ready to use) | • | • |
| Model | Bronze PMX 500 | Infiltration Cu IN |
| Sintering | • | • |
| Friction | ||
| Blasting | ||
| Diamonds Tool | ||
| Welding | ||
| Flame cutting | ||
| Plastic/resin/ceramic filler | ||
| Carbon brush | ||
| Chemical | ||
| Jewellery | ||
| Food/Farmaceutical/Cosmetics | ||
| Magnetic | ||
| Brazing | ||
| Other iron applications | ||
| Soft Blasting |
- Bronze PMX 500
-
Catalogue Sintering
-
Pometon introduction
- Infiltration Cu IN
-
Catalogue Sintering
-
Pometon introduction